Metal Pads with Openings in Integrated Circuits

ABSTRACT

A device includes a metal pad, and a passivation layer including portions overlapping edge portions of the metal pad. A Post-Passivation-Interconnect (PPI) includes a trace portion overlying the passivation layer, and a pad portion connected to the trace portion. A polymer layer includes an upper portion over the PPI, and a plug portion extending into, and encircled by, the pad portion of the PPI.

PRIORITY CLAIM AND CROSS-REFERENCE

This application is a continuation of U.S. patent application Ser. No. 13/764,569, filed Feb. 11, 2013, and entitled “Metal Pads with Openings in Integrated Circuits,” which application claims the benefit of the following provisionally filed U.S. patent application: Application Ser. No. 61/695,206, filed Aug. 30, 2012, and entitled “Metal Pads with Openings in Integrated Circuits,” which applications are hereby incorporated herein by reference.

BACKGROUND

In the formation of integrated circuits, devices such as transistors are first formed at the surface of a semiconductor substrate in a wafer. An interconnect structure is then formed over the integrated circuit devices. A metal pad is formed over, and is electrically coupled to, the interconnect structure. A passivation layer and a first polymer layer are formed on the metal pad, with the metal pad exposed through the openings in the passivation layer and the first polymer layer.

Post-passivation interconnect (PPI) is then formed, followed by the formation of a second polymer layer over the PPI. An Under-Bump-Metallurgy (UBM) is formed extending into an opening in the second polymer layer, wherein the UBM is electrically connected to the PPI. A solder ball is then placed over the UBM and reflowed.

A PPI may include a PPI pad, over which a UBM is formed. Furthermore, the PPI may include a PPI trace that connects the PPI pad to the underlying metal pad.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the embodiments, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:

FIGS. 1 through 8B are cross-sectional views of intermediate stages in the manufacturing of a package in accordance with some exemplary embodiments; and

FIGS. 9A through 9E illustrate the top views of portions of the package, wherein Under-Bump-Metallurgies (UBMs) and holes in Post-Passivation Interconnect (PPI) structure are illustrated.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

The making and using of the embodiments of the disclosure are discussed in detail below. It should be appreciated, however, that the embodiments provide many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are illustrative, and do not limit the scope of the disclosure.

A package comprising a Post-Passivation Interconnect (PPI) structure and the method of forming the same are provided in accordance with some embodiments. The intermediate stages of manufacturing the package in accordance with some embodiments are illustrated. The variations of the embodiments are discussed. Throughout the various views and illustrative embodiments, like reference numbers are used to designate like elements.

Referring to FIG. 1, chip 10, which includes semiconductor substrate 20, is provided. Semiconductor substrate 20 may be a bulk silicon substrate or a silicon-on-insulator substrate. Alternatively, other semiconductor materials that include group III, group IV, and/or group V elements may also be used, which semiconductor materials may include silicon germanium, silicon carbon, and III-V compound semiconductor materials. Integrated circuit devices such as transistors (schematically illustrated as 21) are formed in and/or on semiconductor substrate 20. Chip 10 may further include Inter-Layer Dielectric (ILD) 22 over semiconductor substrate 20, and interconnect structure 24 over ILD 22. Interconnect structure 24 includes metal lines 26 and vias 28, which are formed in dielectric layers 25. The combination of metal lines at a same level is referred to a metal layer hereinafter. In some embodiments, interconnect structure 24 includes a plurality of metal layers that are interconnected through vias 28. Metal lines 26 and vias 28 may be formed of copper or copper alloys, although they can also be formed of other metals. In some embodiments, dielectric layers 25 are formed of low-k dielectric materials. The dielectric constants (k values) of the low-k dielectric materials may be less than about 3.0, or less than about 2.5, for example.

Metal pad 30 is formed over interconnect structure 24, and may be electrically coupled to integrated circuit devices 21 through metal lines 26 and vias 28, wherein lines 29 are illustrated to represent the electrical coupling. Metal pad 30 may be an aluminum pad or an aluminum-copper pad, although other metallic materials may be used. Passivation layer 32 is formed over interconnect structure 24. A portion of passivation layer 32 may cover the edge portions of metal pad 30, and a central portion of metal pad 30 is exposed through an opening in passivation layer 32. Passivation layer 32 may be a single layer or a composite layer, and may be formed of a non-porous material. In some embodiments, passivation layer 32 is a composite layer comprising a silicon oxide layer (not shown), and a silicon nitride layer (not shown) over the silicon oxide layer. Passivation layer 32 may also be formed of other non-porous dielectric materials such as Un-doped Silicate Glass (USG), silicon oxynitride, and/or the like.

Polymer layer 36 is formed over passivation layer 32. Polymer layer 36 may comprise a polymer such as polyimide, BenzoCycloButene (BCB), PolyBenzOxazole (PBO), and the like. The formation methods may include spin coating, for example. Polymer layer 36 may be dispensed in a liquid form, and then cured.

Polymer layer 36 is patterned, and metal via 40 is formed in polymer layer 36. Metal via 40 may overlap and contact the top surface of metal pad 30. Metal via 40 may also include portions extending over and contacting portions of passivation layer 32 in accordance with some embodiments. The top surface of metal via 40 may be level with the top surface of polymer layer 36.

Next, referring to FIG. 2, chip 10 is placed on carrier 42, for example, through adhesive 44. Molding material 46 is then dispensed and cured to mold chip 10 therein. In some embodiments, molding material 46 comprises a molding compound. In alternative embodiments, molding material 46 comprises a molding underfill, a resin, or the like. Next, referring to FIG. 3, a planarization is performed to remove excess portions of molding material 46 over polymer layer 36 and metal via 40 to reveal metal via 40. As a result, top surface 36A of polymer layer 36, top surface 46A of molding material 46, and top surface 40A of metal via 40 are substantially level with each other.

In FIG. 4, polymer layer 48 is formed, which may comprise a polymer selected from the same group of candidate materials as polymer layer 36. Polymer layer 48 thus extends overlapping, and in contact with, polymer layer 36, metal via 40, and molding material 46. Polymer layer 48 is then patterned to form opening 50, through which metal via 40 is exposed. In the embodiments that polymer layer 48 is formed of a photo-sensitive material, polymer layer 48 is patterned by exposing to light through a lithography mask (not shown). The exposed polymer layer 48 is then developed to form opening 50.

FIGS. 5 and 6 illustrate the formation of PPI 52, which is such named since the formation of PPI 52 is after the formation of passivation layer 32. In some embodiments, as shown in FIG. 5, Seed layer 54 is deposited over polymer layer 48, followed by the formation and the patterning of mask 56 over seed layer 54. Seed layer 54 may be a copper layer deposited using Physical Vapor Deposition (PVD), for example. Mask layer 56 may be a dry film or a photo resist. Metal layer 58 is then formed over seed layer 54, as shown in FIG. 6. Metal layer 58 may be formed of pure copper, substantially pure copper, or a copper alloy, and may be formed using plating. After the formation of metal layer 58, mask layer 56 (FIG. 5) is removed. The portions of seed layer 54 overlapped by mask layer 56 are then removed in an etching step. Resulting in the pattern shown in FIG. 6. The remaining portions of seed layer 54 and metal layer 58 are in combination referred to as PPI 52 hereinafter.

PPI 52 includes PPI pad 52A and PPI trace 52B. The lateral dimension (such as width or diameter) of PPI pad 52A is significantly greater than the lateral dimension of PPI trace 52B. For example, FIG. 9A illustrates a top view of exemplary PPI 52. In the embodiments in FIG. 9A, PPI trace 52B has a longitudinal direction in X direction, wherein dimension W2 of PPI pad 52A is greater than three times, five times, or ten times width W1 of PPI trace 52B, wherein widths W1 and W2 are measured in Y direction. In some embodiments, width W1 of PPI trace 52B is substantially uniform.

Referring back to FIG. 6, PPI 52 further includes via portion 52C that extends into opening 50 (FIG. 4) of polymer layer 48 to contact metal via 40. In some embodiments, PPI 52 may extend to overlap chip 10 and molding material 46, as illustrated by dashed lines. Accordingly, the illustrated structure may be a fan-out structure.

As also shown in FIG. 6, PPI 52 may include one or a plurality of openings 60 in PPI pad 52A, wherein openings 60 may be in the transition region of PPI pad 52A and PPI trace 52B. Polymer layer 48 is exposed through openings 60. In some embodiments, no openings 60 are formed in regions other than the transition region. For example, in the portions of PPI pad 52A close to the center 52A1 of PPI pad 52A, no opening is formed. Also, there may not be any opening(s) formed on the portions of PPI pad 52A that are on the opposite side of center 52A1 than PPI trace 52B. Width W3 of openings 60 may be between about 20 percent and about 80 percent of width W1 of PPI trace 52B. It is appreciated, however, that the dimensions recited throughout the description are merely examples, and may be changed to different values.

FIG. 7 illustrates the formation and the patterning of polymer layer 62. Polymer layer 62 may comprise polyimide or another polymer-based material such as PBO, BCB, or the like. In some embodiments, polymer layer 62 is formed using spin coating. Polymer layer 62 comprises portions filled into openings 60 (FIG. 6), which portions of polymer layer 62 are referred to as polymer plugs 62A throughout the description. Furthermore, polymer layer 62 further comprises a portion overlapping PPI 52, and portions encircling PPI 52.

Next, as shown in FIG. 8A, UBM layer 64 is formed. In some embodiments, UBM layer 64 includes a barrier layer (not shown) and seed layer (not shown) over the barrier layer. UBM layer 64 extends into the opening in polymer layer 62, and may further include portions overlapping polymer layer 62. UBM layer 64 may be electrically coupled to, and may be in physical contact with, PPI pad 52A. The barrier layer may be a titanium layer, a titanium nitride layer, a tantalum layer, a tantalum nitride layer, or layers formed of a titanium alloy or a tantalum alloy. The materials of the seed layer may include copper or copper alloys. In some embodiments, UBM layer 64 is formed using PVD or other applicable methods.

Further referring to FIG. 8A, connector 66 is formed. In some embodiments, connector 66 is a metal region, which is either a metal ball, such as a solder ball or a copper ball, placed on UBM layer 64, or a metal pillar formed on UBM layer 64 through plating. In the embodiments wherein connector 66 comprises solder, the solder may go through a reflow process, and metal ball 66 is formed. In alternative embodiments, connector 66 comprises a metal pillar, which may be a copper pillar. Additional layers such as a nickel layer, a solder cap, a palladium layer, and the like, may also be formed on the metal pillar. Chip 10 and molding material may then be demounted from carrier 42 as an integrated package.

FIG. 8B illustrates the cross-sectional view of a package in accordance with alternative embodiments. These embodiments are similar to the embodiments shown in FIG. 8A, except that PPI pad 52A is in the fan-out region of the respective package. PPI pad 52A hence overlaps molding material 46. In additional, polymer plugs 62A may also be in the fan-out region and overlap molding material 46, as shown in FIG. 8B. In alternative embodiments, PPI pad 52A overlaps molding material 46, while a part (and not all) of polymer plugs 62A overlaps molding material 46, and the remaining polymer plugs 62A overlap chip 10.

FIGS. 9A through 9E illustrate top views of exemplary PPI traces 52B, UBMs 64, and metal connectors 66. In each of FIGS. 9A through 9E, openings 60 are formed in PPI pad 52A, and polymer plugs 62A are filled in openings 60. Openings 60/polymer plugs 62A are formed in the transition regions of PPI pad 52A, which transition region is close to PPI trace 52B. For example, the transition regions are where the widths gradually reduce from the width of PPI pads 52A to the width of corresponding connecting PPI traces 52B. In the top views in FIGS. 9A through 9E, PPI pads 52A may have circular shapes, wherein the diameter of the circle is also shown as width W2, although PPI pads 52 may have other shapes such as ellipse, hexagon, rectangle, or the like. The openings 60/polymer plugs 62A having different counts, layouts, sizes are contemplated in the scope of the present disclosure. Furthermore, openings 60/polymer plugs 62A in FIGS. 9A through 9E may be combined, and formed in a same PPI 52 in any combination.

For example, FIG. 9A illustrates openings 60/polymer plugs 62A with diamond shapes or rectangular shapes. In some embodiments, width W3 of openings 60/polymer plugs 62A in FIG. 9A may be between about 20 percent and about 80 percent of width W1 of PPI trace 52B, and may be between about 20 percent and about 80 percent of width W2 of PPI pad 52A. Openings 60/polymer plugs 62A may be laid out as a plurality of columns, which may be either in the X direction and the Y direction. Each column of openings 60/polymer plugs 62A may be aligned to a space between two of the openings 60/polymer plugs 62A in the neighboring column.

FIG. 9B illustrates more openings 60/polymer plugs 62A wither widths W3 smaller than in FIG. 9A. In some embodiments, width W3 in FIG. 9B may be between about 20 percent and about 80 percent of width W1 of PPI trace 52B, and may be between about 20 percent and about 80 percent of width W2 of PPI pad 52A. Again, openings 60/polymer plugs 62A in these embodiments may have a diamond shape, a rectangular shape, or a polygon shape. The openings 60/polymer plugs 62A may be laid out as a plurality of columns, which may extend either in the X direction or the Y direction. Each column and row of openings 60/polymer plugs 62A may be aligned to the openings 60/polymer plugs 62A in the neighboring row and column, respectively.

FIG. 9C illustrates a single opening 60/polymer plug 62A with a great size. In some embodiments, width W3 in FIG. 9C may be between about 20 percent and about 80 percent of width W1, and may be between about 20 percent and about 80 percent of width W2. The single opening 60/polymer plug 62A may be allocated to be aligned to center line 53 of PPI trace 52B, although opening 60/polymer plug 62A may also be misaligned from center line 53. Furthermore, edges 63 of the single opening 60/polymer plug 62A may be substantially parallel to edges 65 of the transition region of PPI 52.

In FIG. 9D, openings 60/polymer plugs 62A have circular top-view shapes. In some embodiments, diameter D1 and/or D2 in FIG. 9D may be between about 20 percent and about 80 percent of width W1, and may be between about 20 percent and about 80 percent of width W2. Furthermore, openings 60/polymer plugs 62A may have diameters D1 and D2 that are different from each other. For example, a ratio of D2/D1 may be between about 0.2 and about 0.8 in accordance with some exemplary embodiments.

The top-view shapes of openings 60/polymer plugs 62A may be any shape including, and not limited to, rectangles or spades (FIGS. 9A through 9C), and circles (FIG. 9D). For example, FIG. 9E illustrates an irregular-shaped opening 60/polymer plug 62A, which have straight edges 63, and curved edge 67. Furthermore, edges 63 of the opening 60/polymer plug 62A may be substantially parallel to edges 65 of the transition region of PPI 52.

In some embodiments, openings 60/polymer plugs 62A are not overlapped by UBM 64 and/or connectors 66. In alternative embodiments, openings 60/polymer plugs 62A may be overlapped by (and hence are directly under) UBM 64 and/or connectors 66. In the illustrative embodiments, openings 60/polymer plugs 62A are formed in fan-out structures, in which PPI 52 may extend beyond the edges of chip 10 to overlap molding material 46. In alternative embodiments, openings 60/polymer plugs 62A may be formed inside chip 10. In which case, metal via 40 and polymer layer 36 may not be formed, and PPI portion 52C as in FIGS. 8A and 8B extends into the opening in polymer layer 48 and passivation layer 32 to contact metal pad 30. In these embodiments, no molding material 46 is dispensed.

In the embodiments, by forming openings in the transitions region of a PPI pad, which transition region is close to a respective connecting PPI trace, the volume of the PPI in the transition region becomes smaller, and the transition region becomes more flexible and less rigid. Since PPI pads are much larger, and hence are much more rigid than PPI traces, the PPI traces suffer from stresses and may crack. By making transition regions less rigid, the transition regions may help absorb the stress, and hence PPI traces are protected from the crack.

In accordance with embodiments, a device includes a metal pad, and a passivation layer including portions overlapping edge portions of the metal pad. A PPI includes a trace portion overlying the passivation layer, and a pad portion connected to the trace portion. A polymer layer includes an upper portion over the PPI, and a plug portion extending into, and encircled by, the pad portion of the PPI.

In accordance with other embodiments, a chip includes a metal pad, a passivation layer comprising portions overlapping edge portions of the metal pad, and a first polymer layer over the metal pad. A molding material encircles the chip. A top surface of the molding material is substantially level with a top surface of the first polymer layer. A PPI is electrically coupled to the metal pad. The PPI includes a trace portion overlying the first polymer layer, and a pad portion overlying the first polymer layer and connected to the trace portion. A second polymer layer includes a cover portion over the PPI, and a plug portion penetrating through the pad portion of the PPI to contact the first polymer layer. A UBM extends into the second polymer layer to contact the pad portion of the PPI.

In accordance with yet other embodiments, a device includes a metal pad, a passivation layer including portions overlapping edge portions of the metal pad, a first polymer layer over the metal pad, and a metal via in the first polymer layer. The metal via overlaps, and is in contact with, the metal pad. A second polymer layer is disposed over the first polymer layer and the metal via. A PPI includes a first portion overlying the second polymer layer, and a second portion extending into the second polymer layer to contact the metal via. A third polymer layer includes a plug portion extending into, and encircled by, the PPI, wherein the plug portion comprises a bottom surface contacting a top surface of the second polymer layer.

Although the embodiments and their advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the embodiments as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, and composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. In addition, each claim constitutes a separate embodiment, and the combination of various claims and embodiments are within the scope of the disclosure. 

What is claimed is:
 1. A method comprising: forming a first polymer layer over a device die; patterning the first polymer layer to reveal a conductive feature in the device die; depositing a blanket seed layer over the first polymer layer and the conductive feature; forming a patterned mask layer over the blanket seed layer, with an opening formed in the patterned mask layer to expose the blanket seed layer, wherein the opening comprises: an elongated portion; a bulk portion wider than the elongated portion; and a transition portion connecting the bulk portion to the elongated portion, wherein the patterned mask layer comprises a discrete portion in the transition portion of the opening; plating a conductive material on exposed portions of the blanket seed layer; removing the patterned mask layer; and etching portions of the blanket seed layer covered by the patterned mask layer, wherein remaining portions of the blanket seed layer and the conductive material form a Post-Passivation Interconnect (PPI).
 2. The method of claim 1, wherein the PPI comprises: a bulk portion; a trace portion; and a transition portion with a through-opening therein.
 3. The method of claim 2 further comprising forming a second polymer layer to cover the PPI, wherein the second polymer layer extends into the through-opening to form a polymer plug.
 4. The method of claim 3 further comprising: encapsulating the device die in an encapsulating material; and planarizing a top surface of the conductive feature and the encapsulating material, wherein the second polymer layer further overlaps the encapsulating material.
 5. The method of claim 3, wherein the polymer plug is in physical contact with a top surface of the first polymer layer.
 6. The method of claim 3, wherein a plurality of discrete polymer plugs comprised in the second polymer layer penetrate through the PPI to contact the first polymer layer, with each of the plurality of discrete polymer plugs encircled, and separated from each other, by the PPI.
 7. The method of claim 1, wherein the discrete portion is aligned to a middle line of the elongated portion, with the middle line extending in a lengthwise direction of the elongated portion.
 8. The method of claim 1 further comprising an electrical connector electrically coupled to the PPI.
 9. A method comprising: encapsulating a device die in an encapsulating material; performing a planarization to level a first top surface of the device die and a second top surface of the encapsulating material with each other; forming a first polymer layer over and in contact with the first top surface and the second top surface; forming an opening in the first polymer layer to expose a conductive feature in the device die; forming a conductive interconnection with a portion extending into the opening, wherein the conductive interconnection comprises: a bulk portion; a trace portion narrower than the bulk portion; and a transition portion with a through-opening therein; and forming a second polymer layer covering the conductive interconnection, wherein the second polymer layer further comprises a polymer plug penetrating through the transition portion.
 10. The method of claim 9, wherein the forming the conductive interconnection comprises: forming a patterned mask layer over the first polymer layer, with a first opening formed in the patterned mask layer, wherein the first opening comprises: an elongated portion; a bulk portion wider than the elongated portion; and a transition portion connecting the bulk portion to the elongated portion, wherein the patterned mask layer comprises a discrete portion in the transition portion of the first opening; and plating a conductive material into the first opening.
 11. The method of claim 9 further comprising: forming a second opening in the second polymer layer; and forming an Under Bump Metallurgy (UBM) penetrating through the second opening to contact the bulk portion of the conductive interconnection.
 12. The method of claim 9, wherein the second polymer layer further comprises a plurality of polymer plugs penetrating through the transition portion, wherein the plurality of polymer plugs is spaced apart from each other by the transition portion of the conductive interconnection.
 13. The method of claim 9, wherein the polymer plug has a bottom surface in contact with a top surface of the first polymer layer.
 14. The method of claim 9, wherein from regions closer to the bulk portion of the conductive interconnection to the regions closer to the trace portion of the conductive interconnection, the transition portion has increasingly smaller widths.
 15. The method of claim 9, wherein in a top view of the conductive interconnection, the transition portion has a substantially straight edge.
 16. A method comprising: forming a first polymer layer over a device die; forming a first opening in the first polymer layer to expose a metal pad in the device die; forming a Post-Passivation Interconnect (PPI) with a portion extending into the first opening, wherein the PPI comprises: a bulk portion; and a trace portion narrower than the bulk portion; and forming a second polymer layer covering the PPI, wherein the second polymer layer further comprises at least one polymer plug penetrating through the PPI; and patterning the second polymer layer to form a second opening exposing a center portion of the bulk portion of the PPI, wherein the at least one polymer plug is between the second opening and the trace portion; and forming conductive features extending into the second opening.
 17. The method of claim 16 further comprising: encapsulating the device die in an encapsulating material; and performing a planarization to level a first top surface of the device die and a second top surface of the encapsulating material, wherein the first polymer layer overlaps both the device die and the encapsulating material.
 18. The method of claim 16, wherein all of the at least one polymer plug are between the second opening and the trace portion.
 19. The method of claim 16, wherein the forming the PPI comprises: forming a blanket seed layer over the first polymer layer. forming a patterned mask layer, with an additional opening formed in the patterned mask layer to expose the blanket seed layer, wherein the additional opening comprises: an elongated portion; a bulk portion wider than the elongated portion; and a transition portion connecting the bulk portion to the elongated portion, wherein the patterned mask layer comprises at least one discrete portion in the transition portion of the additional opening; and plating a conductive material into the additional opening.
 20. The method of claim 16, wherein the at least one polymer plug has a bottom surface in contact with a top surface of the first polymer layer. 